在選擇鐵藝護欄的時候，更關心的容易生銹嗎？而鐵藝護欄在焊接成型之后，會進行防銹處理工藝，接下來我們?yōu)榇蠹以敿氈v解下鐵藝護欄的防銹處理工藝。一、 熱鍍鋅熱鍍鋅是將除銹后的鋼件浸入500℃左右融化的鋅液中，使鋼構件表面附著鋅層，從而起到防腐的目的。熱鍍鋅板的生產工序主要包括：原板準備→鍍前處理→熱浸鍍→鍍后處理→成品檢驗等。

　　When choosing wrought iron guardrails, is it more concerned about rusting? After welding and forming, the wrought iron guardrail will undergo rust prevention treatment. Next, we will explain in detail the rust prevention treatment process of wrought iron guardrail. 1、 Hot dip galvanizing is the process of immersing rust removed steel components in a molten zinc solution at around 500 ℃ to attach a zinc layer to the surface of the steel components, thereby achieving the purpose of corrosion prevention. The production process of hot-dip galvanized sheet mainly includes: original sheet preparation → pre plating treatment → hot-dip coating → post plating treatment → finished product inspection, etc.

　　二、 冷鍍鋅冷鍍鋅也叫電鍍鋅，是利用電解設備將管件經過除油、酸洗、后放入成分為鋅鹽的溶液中，并連接電解設備的負極，在管件的對面放置鋅板，連接在電解設備的正極接通電源，利用電流從正極向負極的定向移動就會在管件上沉積一層鋅，冷鍍管件是先加工后鍍鋅。

　　2、 Cold galvanizing, also known as electroplating, is the process of using electrolytic equipment to remove oil, acid wash, and then place the pipe fittings in a solution composed of zinc salts. The negative electrode of the electrolytic equipment is connected to the negative electrode, and a zinc plate is placed on the opposite side of the pipe fittings. The positive electrode of the electrolytic equipment is connected to the power supply, and the directional movement of current from the positive electrode to the negative electrode deposits a layer of zinc on the pipe fittings. Cold galvanizing pipe fittings are first processed and then galvanized.

　　三、 機械鍍鋅機械鍍鋅在裝有鍍件、玻璃球、鋅粉、水和促進劑的旋轉滾桶內，作為沖擊介質的玻璃球隨著滾桶轉動，與鍍件表面發(fā)生摩擦和錘擊產生機械物理能量，在化學促進劑的作用下，將鍍涂的鋅粉“冷焊”到鍍件表面上，形成光滑、均勻和細致的具有一定厚度的鍍層。

　　3、 Mechanical galvanizing is carried out in a rotating drum containing plated parts, glass balls, zinc powder, water, and accelerators. The glass balls, as the impact medium, rub and hammer against the surface of the plated parts as the drum rotates, generating mechanical physical energy. Under the action of chemical accelerators, the zinc powder coated is "cold welded" to the surface of the plated parts, forming a smooth, uniform, and fine coating with a certain thickness

本文由濟南燕翔鐵藝制品有限公司 友情奉獻.更多有關的知識請點擊:http://www.eastagcn.com.cn/真誠的態(tài)度.為您提供為的服務.更多有關的知識我們將會陸續(xù)向大家奉獻.敬請期待.

This article is a friendly contribution from Jinan Yanxiang Iron Art Products Co., Ltd. For more related knowledge, please click: http://www.eastagcn.com.cn/ Sincere attitude. We provide you with comprehensive services. We will gradually contribute more relevant knowledge to everyone. Please stay tuned